Quantitative analysis of microstructure evolution, stress partitioning and thermodynamics in the dynamic transformation of Fe-14Ni alloy

Li, L.*; 宮本 吾郎*; Zhang, Y.*; Li, M.*; 諸岡 聡; 及川 勝成*; 友田 陽*; 古原 忠*

Journal of Materials Science & Technology, 184, p.221 - 234, 2024/06

https://doi.org/10.1016/j.jmst.2023.10.037

Dynamic transformation (DT) of austenite () to ferrite () in the hot deformation of various carbon steels was widely investigated. However, the nature of DT remains unclear due to the lack of quantitative analysis of stress partitioning between two phases and the uncertainty of local distribution of substitutional elements at the interface in multi-component carbon steels used in the previous studies. Therefore, in the present study, a binary Fe-Ni alloy with + duplex microstructure in equilibrium was prepared and isothermally compressed in + two-phase region to achieve quantitative analysis of microstructure evolution, stress partitioning and thermodynamics during DT. to DT during isothermal compression and to reverse transformation on isothermal annealing under unloaded condition after deformation were accompanied by Ni partitioning. The lattice strains during thermomechanical processing were obtained via in-situ neutron diffraction measurement, based on which the stress partitioning behavior between and was discussed by using the generalized Hooke's law. A thermodynamic framework for the isothermal deformation in solids was established based on the basic laws of thermodynamics, and it was shown that the total Helmholtz free energy change in the deformable material during the isothermal process should be smaller than the work done to the deformable material. Under the present thermodynamic framework, the microstructure evolution in the isothermal compression of Fe-14Ni alloy was well explained by considering the changes in chemical free energy, plastic and elastic energies and the work done to the material. In addition, the stabilization of the soft phase in Fe-14Ni alloy by deformation was rationalized since the to transformation decreased the total Helmholtz free energy by decreasing the elastic and dislocation energies.

Organization of malonamides from the interface to the organic bulk phase

Micheau, C.; 上田 祐生; 元川 竜平; 阿久津 和宏*; 山田 悟史*; 山田 雅子*; Moussaoui, S. A.*; Makombe, E.*; Meyer, D.*; Berthon, L.*; et al.

Journal of Molecular Liquids, 401, p.124372_1 - 124372_12, 2024/05

https://doi.org/10.1016/j.molliq.2024.124372

Supramolecular organization of extractant molecules impacts metal ions separation behavior. Probing bulk and interfacial structures of the relevant systems is expected to provide key insights into the metal ion selectivity and kinetic aspects. The supramolecular features of two solvent extraction systems based on malonamide extractants, N,N,N′,N′-tetrahexylmalonamide (THMA) in toluene and N,N′-dimethyl-N,N′-dibutyl-2-tetradecylmalonamide (DBMA) in n-heptane, were studied using small-angle X-ray scattering for the organic bulk phases, as well as interfacial tension and neutron reflectivity measurements for the interfaces. In the bulk solution, THMA forms dimeric/trimeric associates but no aggregates in toluene, while DBMA forms large aggregates in n-heptane. On the other hand, THMA accumulates in a diffuse layer at the interface at high THMA concentration, whereas DBMA forms a compact but thinner layer. After Pd(II) extraction, the thickness of interfacial layers decreases in the case of THMA, and totally vanishes in the case of DBMA. Based on these new structural information, two mechanisms are proposed for Pd(II) and Nd(III) extraction with malonamides. In toluene, THMA associates slightly accumulate in the vicinity of the interface, then coordinate Pd(II) and diffuse into the organic bulk phase. In n-heptane, DBMA aggregates adsorb at the interface then pick up Nd(III) cations in their polar cores and finally diffuse into the bulk.

First demonstration of a single-end readout position-sensitive optical fiber radiation sensor inside the Fukushima Daiichi Nuclear Power Station based on wavelength-resolving analysis

寺阪 祐太; 佐藤 優樹; 瓜谷 章*

Nuclear Instruments and Methods in Physics Research A, 1062, p.169227_1 - 169227_6, 2024/05

https://doi.org/10.1016/j.nima.2024.169227

We have developed a new position-sensitive optical fiber radiation sensor that achieves single-end readout and high dose rate application. The sensor determines the incident position of radiation on the optical fiber by using the wavelength dependency of light attenuation within the fiber. Through the analysis of the output wavelength spectrum from the fiber end, the incident position of radiation on the optical fiber can be inversely estimated using the spectrum unfolding procedure. Using this optical fiber sensor, we conducted a measurement of radiation distribution inside the Fukushima Daiichi Nuclear Power Station (FDNPS). The actual trend of incident position of radiation was successfully reproduced in a high dose rate area, with a maximum dose rate exceeding 100 mSv/h. This validates the effectiveness of our new position-sensitive optical fiber radiation sensor.

Inelastic neutron scattering study of magnon excitation by ultrasound injection in yttrium iron garnet

社本 真一; 赤津 光洋*; Chang, L.-J.*; 根本 祐一*; 家田 淳一

Applied Physics Letters, 124(11), p.112402_1 - 112402_5, 2024/03

https://doi.org/10.1063/5.0189768

YFeOにおける超音波注入によるマグノン励起を非弾性中性子散乱によって研究した。その結果、縦波と横波の両方で超音波注入によりマグノン励起の非弾性中性子散乱強度が増強されることがわかった。

Quantum critical behavior of the hyperkagome magnet MnCoSi

山内 宏樹; Sari, D. P.*; 安井 幸夫*; 坂倉 輝俊*; 木村 宏之*; 中尾 朗子*; 大原 高志; 本田 孝志*; 樹神 克明; 井川 直樹; et al.

Physical Review Research (Internet), 6(1), p.013144_1 - 013144_9, 2024/02

https://doi.org/10.1103/PhysRevResearch.6.013144

-Mn-type family alloys Mn have three-dimensional antiferromagnetic (AFM) corner-shared triangular network. The antiferromagnet MnRhSi shows magnetic short-range order (SRO) over a wide temperature range of approximately 500 K above the Nel temperature = 190 K. MnCoSi has the smallest lattice parameter and the lowest in the family compounds. The quantum critical point (QCP) from AFM to the quantum paramagnetic state is expected near a cubic lattice parameter of 6.15 of MnCoSi is only 140 K, quantum critical behavior is observed in MnCoSi as the enhancement of the electronic specific heat coefficient . We study how the magnetic SRO appears in MnCoSi by using neutron scattering, SR, and physical property measurements. The experimental results show that the neutron scattering intensity of the magnetic SRO does not change much regardless of the suppressed magnetic moment in the long-range magnetic ordered state compared to those of MnRhSi. The initial asymmetry drop ratio of SR above becomes small, and the magnetic SRO temperature is suppressed to 240 K. The results suggest that the MnCoSi is close to the QCP in the Mn system.

Fe-5Mn-0.1C中Mn鋼におけるリューダース変形中の微視組織および塑性の発達

小山 元道*; 山下 享介*; 諸岡 聡; 澤口 孝宏*; Yang, Z.*; 北條 智彦*; 川崎 卓郎; Harjo, S.

鉄と鋼, 110(3), p.197 - 204, 2024/02

https://doi.org/10.2355/tetsutohagane.TETSU-2023-038

The local plasticity and associated microstructure evolution in Fe-5Mn-0.1C medium-Mn steel (wt.%) were investigated in this study. Specifically, the micro-deformation mechanism during Lders banding was characterized based on multi-scale electron backscatter diffraction measurements and electron channeling contrast imaging. Similar to other medium-Mn steels, the Fe-5Mn-0.1C steel showed discontinuous macroscopic deformation, preferential plastic deformation in austenite, and deformation-induced martensitic transformation during Lders deformation. Hexagonal close-packed martensite was also observed as an intermediate phase. Furthermore, an in-situ neutron diffraction experiment revealed that the pre-existing body- centered cubic phase, which was mainly ferrite, was a minor deformation path, although ferrite was the major constituent phase.

Thermal conductivity measurement of uranium-plutonium mixed oxide doped with Nd/Sm as simulated fission products

堀井 雄太; 廣岡 瞬; 宇野 弘樹*; 小笠原 誠洋*; 田村 哲也*; 山田 忠久*; 古澤 尚也*; 村上 龍敏; 加藤 正人

Journal of Nuclear Materials, 588, p.154799_1 - 154799_20, 2024/01

https://doi.org/10.1016/j.jnucmat.2023.154799

MOX燃料の照射により生成する主要なFPであるNdO及びSmO、模擬FPとして添加したMOXの熱伝導率を評価した。MOX中の模擬FPの均質性の観点から熱伝導率を評価するため、ボールミル法及び溶融法で作製した2種類の粉末を用いて、Nd及びSmの均質性が異なる試料を作製した。模擬FPが均質に固溶した試料では含有量が増加するにしたがってMOXの熱伝導率が低下するが、不均質な模擬FPは影響を及ぼさないことが分かった。熱伝導率に対するNd及びSmの影響を古典的フォノン輸送モデル=(A+BT)を用いてNd/Sm依存性を定量的に評価した結果、A(mK/W)=1.7010 + 0.93C + 1.20C, B(m/W)=2.3910と表された。

遮蔽不要な臨界近接監視システム用ダイヤモンド中性子検出器の要素技術開発(委託研究); 令和4年度英知を結集した原子力科学技術・人材育成推進事業

廃炉環境国際共同研究センター; 高エネルギー加速器研究機構*

JAEA-Review 2023-020, 90 Pages, 2023/12

JAEA-Review-2023-020.pdf:6.59MB

日本原子力研究開発機構(JAEA)廃炉環境国際共同研究センター(CLADS)では、令和4年度英知を結集した原子力科学技術・人材育成推進事業(以下、「本事業」という)を実施している。本事業は、東京電力ホールディングス株式会社福島第一原子力発電所の廃炉等を始めとした原子力分野の課題解決に貢献するため、国内外の英知を結集し、様々な分野の知見や経験を、従前の機関や分野の壁を越えて緊密に融合・連携させた基礎的・基盤的研究及び人材育成を推進することを目的としている。平成30年度の新規採択課題から実施主体を文部科学省からJAEAに移行することで、JAEAとアカデミアとの連携を強化し、廃炉に資する中長期的な研究開発・人材育成をより安定的かつ継続的に実施する体制を構築した。本研究は、令和2年度に採択された研究課題のうち、「遮蔽不要な臨界近接監視システム用ダイヤモンド中性子検出器の要素技術開発」の令和2年度から令和4年度分の研究成果について取りまとめたものである。本研究では、高線環境下(1kGy/h)で動作し、高感度中性子検出感度(数count/nv)を持つ軽量で遮蔽不要な深い未臨界モニターを実現するための要素技術開発を行った。開発要素はダイヤモンドを使用した中性子検出素子、耐放射線集積回路6種類とそれら要素を搭載するモジュール複数枚を開発し、目標性能を確認し当初の目的を達成しただけでなく、6cm径ドライチューブに挿入可能な中性子検出器のモックアップを開発し中性子測定動作実証も行い、予定通りの性能を確認した。まず我々は炉内体系が不明である場合に確実に使用可能な未臨界解析手法としてファインマン法を選択し、"線計測数対中性子計測数の比を1未満に抑えること"を明らかにし、この仕様を満たす中性子検出器のデザインと要素技術の研究開発を推進した。この研究開発を通して、ダイヤモンド検出素子は1kGy/h環境下でも安定動作すること、中性子感度も1cmあたり0.015cps/nvであることを確認し、実用化可能であることを実証した。また開発した全ての信号処理用集積回路は、積分照射線量1MGyまで動作確認を行い、これらの要素技術を組み合わせ1kGy/hの線バックグラウンド環境下での動作試験及び中性子検出試験を行い必要な性能を持っていることも確認した。

Stress evaluation method by neutron diffraction for HCP-structured magnesium alloy

Harjo, S.; Gong, W.; 川崎 卓郎

Quantum Beam Science (Internet), 7(4), p.32_1 - 32_13, 2023/12

https://doi.org/10.3390/qubs7040032

Tensile deformation in situ neutron diffraction of an extruded AZ31 alloy was performed to validate conventional procedures and to develop new procedures for stress evaluation from lattice strains by diffraction measurements of HCP-structured magnesium alloys. Increases in the lattice strains with respect to the applied true stress after yielding largely vary among [] grains. The newly proposed procedure of stress evaluation from the lattice strains shows very high accuracy and reliability by weighting the volume fraction of [] grains and evaluating them in many [] orientations in addition to multiplication by the diffraction elastic constant. When multiple peaks cannot be obtained simultaneously, we recommend to use the 12.1 peak for stress evaluation.

Development of an integrated non-destructive analysis system, Active-N

土屋 晴文; 藤 暢輔; 大図 章; 古高 和禎; 北谷 文人; 前田 亮; 米田 政夫

Journal of Nuclear Science and Technology, 60(11), p.1301 - 1312, 2023/11

https://doi.org/10.1080/00223131.2023.2192529

An integrated active neutron non-destructive analysis (NDA) system, Active-N, was developed to gain knowledge of active neutron NDA techniques that are applicable to measurements of nuclear materials in highly radioactive nuclear fuels. Active-N, equipped with a D-T neutron generator, combines three complementary active neutron NDA techniques: Differential Die-away Analysis (DDA), Prompt Gamma-ray Analysis (PGA), and Neutron Resonance Transmission Analysis (NRTA). In this paper, we provide an overview of Active-N and then demonstrate that the compact NRTA system in Active-N can quantify nuclear materials. Monte Carlo simulations were conducted to determine the design of the compact NRTA system including a moderator, flight tubes, and a detector shield. To investigate how accurately the compact NRTA system determines areal densities in a sample, measurements were performed with a Pu pellet-type sample as well as metallic plate samples of In and Ag. The experimental areal densities of Pu, In and Ag were consistent with those calculated for the individual nuclei. These results show that it is feasible to develop a compact NRTA system capable of determining the contents of nuclear materials in nuclear fuels. This research was implemented under the subsidy for nuclear security promotion of MEXT.